可加工性,良好,通用,无添加剂,光学性能 薄膜挤出,吹塑薄膜 | |
薄膜 | |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
密度 | ASTMD1505 | 0.923 | g/cm3 | |
熔流率(熔体流动速率)(190°C/2.16kg) | ASTMD1238 | 4.0 | g/10min | |
抗张强度(断裂) | ASTMD638 | 11.3 | MPa | |
伸长率(断裂) | ASTMD638 | 650 | % | |
薄膜厚度-经测试 | 30 | um | ||
抗张强度 | MD:断裂,30um | ASTMD882 | 21.6 | MPa |
抗张强度 | TD:断裂,30um | ASTMD882 | 16.7 | MPa |
伸长率 | MD:断裂,30um | ASTMD882 | 300 | % |
伸长率 | TD:断裂,30um | ASTMD882 | 550 | % |
落锤冲击(30um) | ASTMD1709 | 60 | g | |
TensileTearStrength | MD:30.0um | ASTMD1004 | 88.3 | kN/m |
TensileTearStrength | TD:30.0um | ASTMD1004 | 78.5 | kN/m |
薄膜厚度-经测试 | 30 | um | ||
抗张强度 | MD:断裂,30um | ASTMD882 | 21.6 | MPa |
抗张强度 | TD:断裂,30um | ASTMD882 | 16.7 | MPa |
伸长率 | MD:断裂,30um | ASTMD882 | 300 | % |
伸长率 | TD:断裂,30um | ASTMD882 | 550 | % |
落锤冲击(30um) | ASTMD1709 | 60 | g | |
TensileTearStrength | MD:30.0um | ASTMD1004 | 88.3 | kN/m |
TensileTearStrength | TD:30.0um | ASTMD1004 | 78.5 | kN/m |
脆化温度 | ASTMD746 | <-76.0 | °C | |
维卡软化温度 | ASTMD1525 | 87.0 | °C | |
熔融温度 | 内部方法 | 111 | °C | |
雾度(30.0um) | ASTMD1003 | 6.0 | % |
LDPE HANWHA LDPE 5325塑料供应商,长期销售韩国Hanwha(韩华)生产的LDPE原料,以上是“LDPE HANWHA LDPE 5325”塑胶料的物性表参数.近期代理商可转仓交易:中油华北 HDPE FHM9455F1/抚顺石化 其它
瑞典柏力开米 PP均聚 POLYfill PPH GF12030 PD2 填料,玻璃纤维增强材料,30%填料按重量.
意大利AD COMPOUND PP均聚 PERLER® N09H4001B00 填料,滑石填料,40%填料按重量.
巴西布拉斯科 PP均聚 Braskem PP CP 145
美国利安德巴塞尔 PP均聚 Moplen HP421H
美国West Michigan PP共聚 EnviroPro 2510MGF 填料,玻璃矿物.
美国Washington Penn PP均聚 WPP PP PPH3MFQ-1 填料,Washington,Penn,美国Washington,Penn.汽车领域的应用
美国利安德巴塞尔 PP共聚 Softell TKG 300N C11498
美国利安德巴塞尔 PP共聚 Hostacom ERC 161N NATRL
以色列普利朗 PP共聚 RAMOFIN PPC101 热稳定性,注射成型
美国舒尔曼ICO Polymers LLDPE ICORENE® 9106 V0 White 1803 滚塑成型 通用,电气元件
韩国乐天化学 LDPE TITANLENE® LDF 200GG
巴西布拉斯科 HDPE Braskem PE IA-59 U3
美国USI HDPE UNITHENE® LH606-13
英国4plas PP 9C12420 IUV 填料/增强材料,玻璃纤维增强材料,20%填料按重量添加剂,冲击改性剂,紫外线稳定剂,特性,冲击改性,共聚物,化学耦合,抗紫外线性能良好