耐水解性 注射成型 | |
电气/电子应用领域 | |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
比重 | ASTMD792 | 1.53 | g/cm3 | |
熔流率(熔体流动速率)(250°C/2.16kg) | ASTMD1238 | 13 | g/10min | |
收缩率-流动 | ASTMD955 | 0.40to1.0 | % | |
吸水率(23°C,24hr) | ASTMD570 | 0.080 | % | |
TensileStrength2(Break,3.20mm) | ASTMD638 | 123 | MPa | |
伸长率2(断裂,3.20mm) | ASTMD638 | 3.0 | % | |
弯曲模量3(3.20mm) | ASTMD790 | 7850 | MPa | |
弯曲强度4(屈服,3.20mm) | ASTMD790 | 196 | MPa | |
悬壁梁缺口冲击强度(23°C,6.40mm) | ASTMD256 | 78 | J/m | |
载荷下热变形温度(0.45MPa,未退火,6.40mm) | ASTMD648 | 215 | °C | |
载荷下热变形温度(1.8MPa,未退火,6.40mm) | ASTMD648 | 210 | °C | |
熔融峰值温度 | ASTMD3418 | 223 | °C | |
RTIElec | UL746 | 140 | °C | |
RTIImp | UL746 | 130 | °C | |
RTIStr | UL746 | 140 | °C | |
体积电阻率 | ASTMD257 | 1.0E+16 | ohmscm | |
介电强度(1.00mm) | ASTMD149 | 28 | kV/mm | |
耐电弧性 | ASTMD495 | PLC5 | ||
相比耐漏电起痕指数(CTI)4 | UL746 | PLC0 | ||
漏电起痕指数(解决方案A) | IEC60112 | 600 | V | |
UL阻燃等级 | 0.71mm | UL94 | HB | |
UL阻燃等级 | 1.5mm | UL94 | HB | |
UL阻燃等级 | 3.3mm | UL94 | HB |
PBT GP2300R塑料供应商,长期销售韩国LG化学生产的PBT原料,以上是“PBT Lupox® GP2300R”塑胶料的物性表参数.近期代理商可转仓交易:美国RTP PPA RTP 4006 A FR 填料,玻璃纤维增强材料,35%填料按重量.
意大利拉题 PEEK Latiohm 88/10-06 CNT 填料,碳纳米填料.
德国朗盛 EPDM Keltan® 6260Q DE 窄分子量分布
美国RTP POM共聚 RTP 800 注射成型
日本宝理 POM共聚 DURACON® M450S 快的成型周期,流动性高,注射成型
日本大赛璐 PC Novalloy-S S1500 (Type G)
印度GLS PC GLS PC MG26 填料,玻璃纤维增强材料,10%填料按重量.
日本三菱 PC XANTAR® G4F 25 R 填料,玻璃纤维增强材料,20%填料按重量.
韩国可隆 PC KOPHOS® KO1365H 挤出,注射成型
日本帝人 PC Multilon® T-2854 耐低温冲击,高耐热性,注射成型 汽车仪表板
马来西亚CIPC PBT FRblend® PBT-1309 填料,玻璃,碳纤维增强材料.电气/电子应用领域
韩国可隆 PBT SPESIN® KP213G15 填料,玻璃纤维增强材料,15%填料按重量.
荷兰帝斯曼 PBT Arnite® TV4 261 /A 填料,玻璃纤维增强材料,30%填料按重量.
美国UniPlas PA66 LCA® N66-408 Type 冲击改性,润滑,注射成型
巴西Petropol PA66 Nypol® PA A3 G38 HS UV RH PRTA011 NR447 填料,玻璃纤维增强材料,38%填料按重量.
● PBT 沙伯基础 VALOX V3500EX resin
良好的流动性,阻燃性,注射成型
● PBT 美国杜邦 ST830FR NC010 其它
● PBT 泰科纳 3409HR
注塑
● PBT 德国赢创(德固赛) VESTODUR 2000
● PBT 日本宝理 DURANEX 3200
填料:玻璃纤维增强材料, 20% 填料按重量。