低粘度,脱模性能良好,耐热性,高,清晰度,高,抗撞击性,良好 | |
光学数据存储 | |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
比重 | ASTMD792 | 1.20 | g/cm3 | |
熔流率(熔体流动速率)(300°C/1.2kg) | ASTMD1238 | 70 | g/10min | |
收缩率-流动 | ASTMD955 | 0.50to0.70 | % | |
吸水率(23°C,24hr) | ASTMD570 | 0.15 | % | |
吸水率(平衡,23°C,50%RH) | ASTMD570 | 0.32 | % | |
拉伸模量 | ASTMD638 | 2300 | MPa | |
抗张强度2(屈服,23°C) | ASTMD638 | 60.0 | MPa | |
抗张强度(断裂) | ASTMD638 | 48.0 | MPa | |
伸长率(屈服) | ASTMD638 | 6.0 | % | |
伸长率(断裂) | ASTMD638 | 60 | % | |
弯曲模量 | ASTMD790 | 2500 | MPa | |
弯曲强度 | ASTMD790 | 100 | MPa | |
NotchedIzodImpact3(23°C,3.20mm) | ASTMD256 | 270 | J/m | |
InstrumentedDartImpact4(23°C,3.20mm,TotalEnergy) | ASTMD3763 | 520 | J | |
DeflectionTemperatureUnderLoad(0.45MPa,Annealed,4.00mm) | ASTMD648 | 137 | °C | |
DeflectionTemperatureUnderLoad(1.8MPa,Unannealed,4.00mm) | ASTMD648 | 124 | °C | |
维卡软化温度 | ASTMD15255 | 147 | °C | |
线形热膨胀系数-流动(-40到82°C) | ASTMD696 | 6.8E-5 | cm/cm/°C | |
折射率 | ASTMD542 | 1.583 | ||
透射率 | ASTMD1003 | 91.0 | % |
PC 1080-70塑料供应商,长期销售韩国LG化学生产的PC原料,以上是“PC Lupoy® 1080-70”塑胶料的物性表参数.近期代理商可转仓交易:台湾定欣 SEBS DIOSHY® GP-845CN-1 填料,DIOSHY,台湾定欣.
意大利Guarniflon PTFE Flontech® FT-GL15-M5-6 填料,玻璃纤维增强材料,15%填料按重量.
德国BARLOG plastics PPS KEBATRON® PPS L1065X3 填料,玻璃矿物,65%填料按重量.
韩国乐天化学 PPA Infino HA-4350G 填料,玻璃纤维增强材料.
美国RTP PEI RTP 2183 LF 填料,碳纤维增强材料,20%填料按重量.
比利时索尔维 PEEK KetaSpire® KT-820 SL30
美国Tyne POM共聚 TYNEA 900 通用
沙伯基础 PPO(PPE) LNP™ LUBRICOMP™ ZFL34 compound 填料,玻璃纤维增强材料,20%填料按重量.
意大利Vamp Tech POM共聚 DENILUB M 00U 20TFSi 润滑
韩国LG化学 PC Lupoy® GN5001RF 阻燃性,无卤,良好的流动性,注射成型 电气/电子应用领域
沙伯基础 PC LEXAN™ 164R resin
美国RTP PC RTP 385 TFE 15 填料,碳纤维增强材料,30%填料按重量.
韩国三养 PC TRIREX® Compound 3025UAS
沙伯基础 PBT VALOX™ 337 resin 耐低温冲击,注射成型 汽车领域的应用,汽车的发动机罩下的零件
沙伯基础 PBT LNP™ THERMOCOMP™ WF0039U compound 填料,玻璃纤维增强材料,15%填料按重量.
● PC 沙伯基础(原GE) LUX9130T
阻燃,注塑
● PC 日本帝人 Panlite G-3420R
填料:玻璃纤维增强材料, 20% 填料按重量。
● PC 美国RTP RTP EMI 331 G FR
填料:不锈钢纤维,玻璃纤维增强材料, 10% 填料按重量。
● PC 美国RTP RTP ESD 385
填料:碳纤维增强材料, 30% 填料按重量。
● PC 德国科思创 Makrolon DP1-1821
纯度高,脱模性能良好,粘度高,注射成型