性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
比重 | ASTMD792 | 1.41 | g/cm3 | |
熔流率(熔体流动速率)(190°C/2.16kg) | ASTMD1238 | 42 | g/10min | |
收缩率-流动 | ASTMD955 | 2.3 | % | |
吸水率(平衡,23°C,60%RH) | ASTMD570 | 0.22 | % | |
抗张强度(23°C) | ASTMD638 | 60.0 | MPa | |
伸长率(断裂,23°C) | ASTMD638 | 50 | % | |
弯曲模量(23°C) | ASTMD790 | 2500 | MPa | |
弯曲强度(23°C) | ASTMD790 | 85.0 | MPa | |
悬壁梁缺口冲击强度(23°C) | ASTMD256 | 50 | J/m | |
洛氏硬度(M级) | ASTMD785 | 80 | ||
载荷下热变形温度(0.45MPa,未退火) | ASTMD648A | 158 | °C | |
载荷下热变形温度(1.8MPa,未退火) | ASTMD648A | 110 | °C | |
维卡软化温度 | ASTMD1525 | 162 | °C | |
熔融温度 | ASTMD1525 | 166 | °C | |
线形热膨胀系数-流动 | ASTMD696 | 1.3E-5 | cm/cm/°C | |
表面电阻率 | ASTMD257 | 1.0E+16 | ohms | |
体积电阻率 | ASTMD257 | 1.0E+14 | ohmscm | |
介电强度 | ASTMD149 | 19 | kV/mm | |
介电常数 | ASTMD150 | 3.70 | ||
耗散因数(1MHz) | ASTMD150 | 6.0E-3 | ||
UL阻燃等级 | UL94 | HB |
POM共聚 KH702GN塑料供应商,长期销售韩国可隆生产的POM共聚原料,以上是“POM共聚 KOCETAL® KH702GN”塑胶料的物性表参数.近期代理商可转仓交易:中国苏州奥斯汀 TPU聚脂 Texalan® 2 Series 282A 抗撞击性高,高拉伸强度,耐低温,高弹性良好,耐磨损性,耐油性能,吹塑成型,薄膜挤出,压延,挤出,注射成型,共挤出成型
美国道康宁Multibase TPE Multi-Flex® TPE SIE A4013 CU1 抗紫外线性能良好,耐用性 汽车领域的应用
美国Network Polymers TPE Softflex® 4494 包覆成型
意大利SO.F.TER SEBS Laprene® 83CS91555/C3
日本旭化成弹性体 SEBS Tuftec™ H1221
美国Dynasol SBS Solprene® 4318
美国塞拉尼斯 EVA Ateva® 1081 高强度,共聚物,良好的热封性,薄膜挤出 薄膜
中国成都乐天 PPS LTP CE-2202
美国杜邦 PPA Zytel® HTN FR52G30NH BK337 填料,玻璃纤维增强材料,30%填料按重量.
沙伯基础 PEI ULTEM™ 1000F resin
日本东丽 PPS Torelina® A515 填料,玻璃纤维增强材料,30%填料按重量.
日本宝理 POM共聚 DURACON® WR-01 防潮性,注射成型
美国Nytef POM均聚 UNITAL® H BK
日本出光 PC TARFLON™ G1910 填料,玻璃纤维增强材料,10%填料按重量.
美国RTP PC RTP EMI 333 G FR 填料,不锈钢纤维,15%填料按重量,玻璃纤维增强材料,20%填料按重量.
● POM共聚 美国RTP RTP 883 TFE 20
填料:碳纤维增强材料, 20% 填料按重量。
● POM共聚 韩国可隆 KOCETAL GF704
填料:玻璃纤维增强材料。
● POM共聚 日本旭化成 Tenac-C 8520
低粘度,流动性高,共聚物
● POM共聚 德国巴斯夫 Ultraform W 2320 003 BK120 Q600
● POM共聚 日本旭化成 Tenac-C 7520
低粘度,共聚物,流动性高