性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
比重 | ASTMD792 | 1.12 | g/cm3 | |
收缩率-流动(3.18mm) | ASTMD955 | 0.30 | % | |
吸水率(23°C,24hr) | ASTMD570 | 0.030 | % | |
洛氏硬度(R级) | ASTMD785 | 95 | ||
拉伸模量 | ASTMD638 | 6890 | MPa | |
抗张强度 | 屈服 | ASTMD638 | 48.3 | MPa |
抗张强度 | —— | ASTMD638 | 42.0 | MPa |
伸长率(断裂) | ASTMD638 | 2.3 | % | |
弯曲模量 | ASTMD790 | 5510 | MPa | |
弯曲强度 | —— | ASTMD790 | 65.0 | MPa |
弯曲强度 | 屈服 | ASTMD790 | 62.1 | MPa |
压缩强度 | ASTMD695 | 57.9 | MPa | |
悬壁梁缺口冲击强度(3.18mm) | ASTMD256 | 69 | J/m | |
无缺口悬臂梁冲击(3.18mm) | ASTMD4812 | 240 | J/m | |
载荷下热变形温度 | 0.45MPa,未退火 | ASTMD648 | 152 | °C |
载荷下热变形温度 | 1.8MPa,未退火 | ASTMD648 | 146 | °C |
线形热膨胀系数-流动 | ASTMD696 | 3.8E-5 | cm/cm/°C | |
导热系数 | ASTMC177 | 0.33 | W/m/K | |
体积电阻率 | ASTMD257 | 1.0E+15 | ohmscm | |
介电强度 | ASTMD149 | 21 | kV/mm | |
介电常数(1MHz) | ASTMD150 | 2.90 | ||
耗散因数(1MHz) | ASTMD150 | 1.0E-3 | ||
耐电弧性(1.59mm) | ASTMD495 | 120 | sec | |
UL阻燃等级(1.6mm,ValuesperRTPCompanytesting.) | UL94 | HB |
PP RTP 105Z塑料供应商,长期销售美国RTP生产的PP原料,以上是“PP RTP 105Z”塑胶料的物性表参数.近期代理商可转仓交易:法国AD MAJORIS PP MAJORIS GFRH300 BLACK 8229
韩国GS加德士 PP Caltex PP HLG41S 填料,长玻璃纤维.家电部件,汽车领域的应用,电气元件
中国宁波竹源新材料 PP Bamtac BPP340A
美国科慕化学 含氟聚合物 Teflon® FFR 750
美国Washington Penn TPO WPP TPO TPO-277 P Black 填料,Washington,Penn,美国Washington,Penn.汽车领域的应用,汽车外部零件
中国深圳盛嘉伦 TPE Gallonprene® GP420-8003 可喷涂的,无卤,高光,注射成型 玩具,包覆成型,柔软的把手
● PP 利安德巴塞尔 CA 1110 G4 LS/4
矿物填料, 10% 填料按重量、良好的刚性、抗冲共聚物、高抗撞击性、抗紫外线性能良好、流动性高、收缩性低、外观良好、无毒性
● PP 李长荣化工(福聚) SP32
良好的刚性、共聚物、高抗撞击性、良好的成型性能
● PP 利安德巴塞尔 RP448S
性能特点:抗撞击性良好, 流动性高,清晰度高,无规共聚物用途:容器加工方法:拉伸吹塑成型,注射成型
● PP 美国陶氏 5A10 其它
● PP 菲利浦 HLN-350
均聚物,热稳定,核化