热稳定 其它 注塑 | |
滑石填料, 20% 填料按重量,热稳定性 |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
比重 | ASTM D792 | 1.05 | g/cm3 | |
成型收缩率 | 3.18 mm | ASTM D955 | 1.2 | % |
吸水率 | 24 hr, 23°C | ASTM D570 | 0.03 | % |
压缩强度 | ASTM D695 | 47.6 | MPa | |
洛氏硬度 | ASTM D785 | 90 | ||
拉伸模量 | ASTM D638 | 2550 | MPa | |
抗张强度 | ASTM D638 | 34.5 | MPa | |
断裂伸长率 | ASTM D638 | 5.0 | % | |
弯曲模量 | ASTM D790 | 2140 | MPa | |
弯曲强度 | ASTM D790 | 53.8 | MPa | |
悬壁梁缺口冲击强度 | 3.18 mm | ASTM D256 | 32 | J/m |
无缺口悬臂梁冲击 | 3.18 mm | ASTM D256 | 246 | J/m |
热变形温度 | 0.45MPa, 未退火 | ASTM D648 | 121 | °C |
热变形温度 | 1.8 MPa, 未退火 | ASTM D648 | 71.1 | °C |
阻燃等级 | UL 94 | HB | ||
线形膨胀系数 | ASTM D696 | 0.000059 | cm/cm/°C | |
导热系数 | ASTM C177 | 0.26 | W/m/K | |
耗散因数 | 1 MHz | ASTM D150 | 0.004 | |
介电常数 | 1 MHz | ASTM D150 | 2.4 | |
介电强度 | ASTM D149 | 20 | kV/mm | |
体积电阻率 | ASTM D257 | 1.0E+16 | ohmcm | |
耐电弧性 | ASTM D495 | 125 | sec | |
螺筒后部温度 | 218-274 | °C | ||
螺筒中部温度 | 218-274 | °C | ||
螺筒前部温度 | 218-274 | °C | ||
干燥温度 | 82.2 | °C | ||
干燥时间 | 2.0 | hr | ||
模具温度 | 32.2-65.6 | °C | ||
注塑温度 | 68.9-103 | MPa | ||
建议的最大回制料比例 | 20 | % |
PP 128 Z塑料供应商,长期销售美国RTP生产的PP原料,以上是“PP 128 Z”塑胶料的物性表参数.近期代理商可转仓交易:墨西哥Grupo IDESA GPPS K-3-L-02 良好的尺寸稳定性,介质流 装饰件,玩具
BP PP HB3152 挤出 绳,地毯背衬,土工布
荷兰DexPlastomer LLDPE 08-076 F 优良的密封性能,高柔性抗裂性和抗环境应力裂纹,非常低的凝胶计数 液体食品包装,洗衣粉包装,挤出涂层结构,其他多层概念
美国Buckeye TPE FLEX A6310 BLK 优秀低温性能,高拉伸强度,高级耐臭氧性 阀门-密封件
美国福禄 PP LPP40BD25GY 碳酸钙填料,40%填料按重量,均聚物
美国RTP PC 304 HF Z 注塑
德国胶宝 TPE K TF2STT 其它
美国杜邦 PA66 105F BK010 (Dry) 注塑
美国Spartech PP PP5240 碳酸钙填料40%,良好的刚性,抗撞击性,着色性,高光泽
欧洲VTC TPE SEBS 650700 耐热性高
西班牙Merquinsa TPU 101 纺织应用,涂敷应用,鞋类,织物
浙江俊尔 PA6 A3-16-2 增强,阻燃,注塑
沙特sabic PPA UF008AR 注塑
美国RTP PA66 203 TFE 18 SI 2 玻纤增强,注塑
捷克Unipetl RPA PP NB425 纤维 无纺布
● PP 道达尔(美国) 3378
良好的颜色稳定性高清晰度低残值
● PP 法国道达尔 4320WZ
良好的刚性和出色的耐冲击性能,再加上高抗蠕变性。
● PP 日本住友 H503E
聚烯烃系复合树脂,UL94V-2级,适合阻燃性的制品
● PP 利安德巴塞尔 HP552K
高拉伸强度,均聚物,抗气体褪色性,良好的拉伸性,良好的撕裂强度
● PP 美国利安德巴塞尔 Clyrell EC390T