其它 其它 注塑 | |
玻璃珠\玻璃纤维,矿物填料,化学耦合 |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
比重 | ASTM D792 | 1.14 | g/cm3 | |
成型收缩率 | 3.18 mm, 注塑 | ASTM D955 | 0.5 | % |
6.35 mm, 注塑 | ASTM D955 | 0.5 | % | |
吸水率 | 24 hr, 23°C | ASTM D570 | 0.03 | % |
洛氏硬度 | ASTM D785 | 100 | ||
拉伸模量 | 注塑 | ASTM D638 | 4820 | MPa |
抗张强度 | ASTM D638 | 52.0 | MPa | |
伸长率 | 屈服, 注塑 | ASTM D638 | 4.0 | % |
弯曲模量 | 注塑 | ASTM D790 | 4130 | MPa |
弯曲强度 | 注塑 | ASTM D790 | 79.0 | MPa |
压缩强度 | ASTM D695 | 58.0 | MPa | |
悬壁梁缺口冲击强度 | 3.18 mm, 注塑 | ASTM D256 | 59.0 | J/m |
无缺口悬臂梁冲击 | 3.18 mm | ASTM D256 | 401 | J/m |
热变形温度 | 0.45 MPa, 未退火 | ASTM D648 | 154 | ℃ |
热变形温度 | 1.8 MPa, 未退火 | ASTM D648 | 143 | ℃ |
线形膨胀系数 | ASTM D696 | 0.000045 | cm/cm/°C | |
导热系数 | ASTM C177 | 0.33 | W/m/K | |
阻燃等级 | UL 94 | HB | ||
体积电阻率 | ASTM D257 | 1.0E+17 | ohmcm | |
介电强度 | ASTM D149 | 220 | kV/mm | |
介电常数 | 1 MHz | ASTM D150 | 2.9 | |
耗散因数 | 1 MHz | ASTM D150 | 0.003 | |
耐电弧性 | ASTM D495 | 125 | sec | |
模具温度 | 32.0-66.0 | ℃ | ||
注塑温度 | 69.0-103 | MPa | ||
螺筒后部温度 | 193-227 | ℃ | ||
螺筒中部温度 | 193-227 | ℃ | ||
螺筒前部温度 | 193-227 | ℃ |
PP 178 UV塑料供应商,长期销售美国RTP生产的PP原料,以上是“PP 178 UV”塑胶料的物性表参数.近期代理商可转仓交易:意大利埃尼 PC 254 注塑
德国雷曼福斯 PA66 1-7180/EG 低摩擦系数经润滑,耐磨损性良好热稳定性,粘度,高 齿轮,纺织应用,工程配件,开关,汽车领域的应用,营业设备,轴承
美国Styron PP DLGF 9631.01 Z 长玻璃纤维,60%填料按重量
奥地利SAX PP PPH118T30 滑石填料30%,均聚物
日本JPC LLDPE SH520 己烯共聚单体
泰国TPI LDPE ST 1018 可加工性良好,可流动性良好,收缩性低,FDA,21,CFR,177,1520 薄壁部件,母料,盖子,玩具,装饰品
美国RTP PC 303 SI 2 注塑
欧洲VTC TPE SEBS 602701 降噪,抗紫外线性能良好,良好粘结性,耐臭氧性能,耐气候影响性能良好,热稳定性,食品接触的合规性
美国杜邦 PA66 70G13HS1L BK031 (Dry) 玻纤增强,注塑
美国RTP PA66 EMI 281 经镍涂覆的碳纤维,10%重量比
美国福禄 PP LPP30BK94HB 碳酸钙填料,30%填料按重量,共聚物
德国巴斯夫 TPU 1154 D 10 抗菌,耐水解性
美国RTP PA66 203 MG 20 TFE 15 玻纤增强,注塑
美国陶氏 PC 300 6 MFR 注塑
慈溪国之光 PPO 01F72 阻燃,耐高温,符合ROHS指令 电子电器壳体,充电器壳体,LED套件
● PP 菲利浦 HLN-120-01
均聚物,核化
● PP 日本三菱 PF341A
薄膜
● PP 美国利安德巴塞尔 Clyrell EC390T
● PP 利安德巴塞尔 RP913J
刚性高、无规共聚物、中等透明度
● PP 利安德巴塞尔 ERC 2014P C1V301
刚性良好 共聚物 抗划伤性高抗紫外线性能良好 流动性高