美国亨斯迈 TPU聚脂 IROGRAN® A 60 E 4902

TPU聚脂 IROGRAN® A 60 E 4902 应用
美国亨斯迈 TPU聚脂 IROGRAN® A 60 E 4902 物理特性
性能项目 试验条件[状态] 测试方法 测试数据
比重2 ASTMD792 1.14 g/cm3
密度3 DIN53478 1.14 g/cm3
MeltVolume-FlowRate(MVR)(160°C/8.7kg) 35.0 cm3/10min
Abrasion2 —— DIN53516 43 mm3
Abrasion2 —— ASTMD395 43 mm3
弹性体 TestMethod NominalValue Unit
TensileSet3(200%Strain) ASTMD412 8 %
TensileSet3(200%Strain) DIN53504 8 %
TensileStress4(100%Strain,0.635mm) ASTMD412 2.34 MPa
TensileStress4(100%Strain,0.635mm) DIN53504 1.40 MPa
TensileStress4(300%Strain,0.635mm) ASTMD412 4.07 MPa
TensileStress4(300%Strain,0.635mm) DIN53504 2.40 MPa
TensileStrength4(Break,0.635mm) ASTMD412 7.52 MPa
TensileStress4(Break,0.635mm) DIN53504 10.0 MPa
TensileElongation4(Break,0.635mm) ASTMD412 720 %
TensileElongation4(Break,0.635mm) DIN53504 900 %
TearStrength4(0.635mm) ASTMD624 35.9 kN/m
TearStrength4(0.635mm) DIN53515 25 kN/m
压缩永久变形2 23°C,70hr ASTMD395 40 %
压缩永久变形2 70°C,24hr ASTMD395 80 %
压缩永久变形2 23°C,70hr DIN53517 35 %
压缩永久变形2 70°C,24hr DIN53517 60 %
巴肖氏弹性 ASTMD2632 60 %
肖氏硬度 邵氏A,注塑 ASTMD2240 56
肖氏硬度 邵氏D,注塑 ASTMD2240 15
肖氏硬度 邵氏A,注塑 DIN53505 55
肖氏硬度 邵氏D,注塑 DIN53505 15
熔融温度 InternalMethod 98.9to130 °C
TMA4 High:635.0um InternalMethod 145 °C
TMA4 Low:635.0um InternalMethod 110 °C

TPU聚脂 A 60 E 4902塑料供应商,长期销售美国亨斯迈生产的TPU聚脂原料,以上是“TPU聚脂 IROGRAN® A 60 E 4902”塑胶料的物性表参数.近期代理商可转仓交易：美国福禄 PP GAPEX® RPP20EU04NA 填料,玻璃纤维增强材料,20%填料按重量.
美国Honeywell PCTFE Honeywell Halar E2000
意大利SO.F.TER TPV Forprene® 6NE001A75 挤出
中国浙江华峰 TPU聚脂 Huafon HF-3H95RL
美国Star TPE StarPrene® 6201-87
德国凯柏胶宝 TPE THERMOLAST® V TV6VAN (Series: LTP/PA)
美国Teknor Apex TPE Monprene® CP-19129
美国Kraton SBS KRATON® D1192 A
英国ELASTO SEBS Dryflex® T709
美国华美化学 EVA ELEVATE™ EF522
意大利Crosspolimeri EVA FRAGOM PR/550
意大利Guarniflon PTFE Flontech® FT-WM20-1 填料,无机填料.
美国Techmer PEEK Plaslube® PEEK CF35 TL5 A 填料,碳纤维增强材料.
美国RTP PPA RTP 4099X68912A 填料,长玻璃纤维,40%填料按重量.
英国威格斯 PEEK VICTREX® PEEK 90CA30

  • 相关产品