性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
密度 | ASTMD1505 | 0.949 | g/cm3 | |
熔流率(熔体流动速率)2 | 190°C/2.16kg | ASTMD1238 | 0.040 | g/10min |
熔流率(熔体流动速率)2 | 190°C/21.6kg | ASTMD1238 | 7.0 | g/10min |
抗张强度(屈服) | ASTMD638 | 24.1 | MPa | |
抗张强度(断裂) | ASTMD638 | 35.2 | MPa | |
伸长率(断裂) | ASTMD638 | 800 | % | |
弯曲模量-2%正割 | ASTMD790 | 1010 | MPa | |
CreepRuptureStrength3(-7°C) | ASTMD1598 | >200 | hr | |
流体静力学设计基础 | 23°C | ASTMD2837 | 11.0 | MPa |
流体静力学设计基础 | 60°C | ASTMD2837 | 6.89 | MPa |
NotchPipeTest4(80°C,102mm) | ISO13479 | >3.4 | month | |
ResistancetoRapidCrackPropagation,Pc5(0°C,102mm) | ISO13477 | >12.0 | bar | |
ResistancetoRapidCrackPropagation,Tc-5bar5(102mm) | ISO13477 | <-7 | °C | |
脆化温度 | ASTMD746 | <-60.0 | °C | |
补充信息 | TestMethod | NominalValue | Unit | |
DSCInductionTemperature | ASTMD3350 | 250 | °C | |
MinimumRequiredStrength(20°C) | ISO12162 | 10.0 | MPa | |
PENT-at2.4MPA(80°C) | ASTMF1473 | >2000 | hr |
HDPE L4904塑料供应商,长期销售美国利安德巴塞尔生产的HDPE原料,以上是“HDPE Alathon® L4904”塑胶料的物性表参数.近期代理商可转仓交易:美国利安德巴塞尔 PP均聚 Moplen EP310DC
美国KMI PP均聚 KMI PP KM-0284ZW 抗冲共聚物,成核的,注射成型,复合 薄壁部件,家用货品,复合
美国利安德巴塞尔 PP均聚 Moplen HP2674
美国RheTech PP共聚 RheTech Polypropylene HP521-00UV 填料,滑石填料,15%填料按重量.
美国舒尔曼 PP共聚 PERCOM® FCS05HI 流动性低,抗撞击性高,抗冲共聚物,型材挤出成型 型材
印度Haldia PP共聚 Halene P B200
美国利安德巴塞尔 LDPE Lupolen 2420 K 光学性能,可加工性良好,吹塑薄膜,注射成型,流延薄膜,挤出涂层 流延薄膜,保护涂料,涂层应用,薄膜,食品包装,收缩性薄膜
法国TOTAL石化 LLDPE TOTAL Polyethylene Lumicene® M 1810 EP
美国MPI LDPE MARPOL® LDF 724-SBV
以色列普利朗 HDPE METALCAP PL380Z81 填料,矿物填料,81%填料按重量.
上海华合 PA6 PA6+20%CF 20%碳纤增强
浙江华峰 PUR JF-A-2062 抗溶剂性,快速固化,良好粘结性
北欧化工 PP RE816CF 包覆,薄膜,医用
美国Epoxies PUR 60-7111 抗撞击性,高,良好的柔韧性,良好粘结性,耐气候影响性能良好,吸水低或不吸水 电气/电子应用领域,电气元件,粘合剂
美国AZDEL PP SL552000-100 (2.0mm) 含有的填充物为55%长玻璃纤维
● HDPE 韩国乐天化学 TITANZEX HM5000
● HDPE 美国利安德巴塞尔 Petrothene LB560401
抗撞击性高,高拉伸强度
● HDPE 美国英力士 B53-35H-124
抗静电,共聚物,良好的强度,高级文化权利(应力裂纹抗拒)
● HDPE 瑞士英力士 Rigidex HM5420XPH
● HDPE LG化学 ME5000
冲击强度高,耐环境应力性好