性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
密度 | ASTMD1505 | 0.953 | g/cm3 | |
表观密度 | ASTMD1895 | 0.53to0.59 | g/cm3 | |
熔流率(熔体流动速率)(190°C/2.16kg) | ASTMD1238 | 7.3 | g/10min | |
SpiralFlow2,3 | InternalMethod | 22.6 | cm | |
拉伸模量4 | —— | ASTMD638 | 1040 | MPa |
拉伸模量4 | 1%正割 | ASTMD638 | 823 | MPa |
抗张强度6(屈服) | ASTMD638 | 28.5 | MPa | |
TensileStrength5(Break) | ASTMD638 | 20.6 | MPa | |
TensileElongation5(Yield) | ASTMD638 | 9.0 | % | |
TensileElongation5(Break) | ASTMD638 | 1200 | % | |
弯曲模量6 | —— | ASTMD790 | 1410 | MPa |
弯曲模量6 | 1%正割 | ASTMD790 | 1300 | MPa |
弯曲模量6 | 2%正割 | ASTMD790 | 1090 | MPa |
悬壁梁缺口冲击强度(23°C) | ASTMD256 | 39 | J/m | |
无缺口悬臂梁冲击(-18°C) | ASTMD4812 | NoBreak | ||
肖氏硬度(邵氏D) | ASTMD2240 | 71 | ||
载荷下热变形温度(0.45MPa,未退火) | ASTMD648 | 72.2 | °C | |
维卡软化温度 | ASTMD1525 | 127 | °C | |
熔融峰值温度 | ASTMD3418 | 130 | °C | |
结晶峰温度(DSC)12 | ASTMD3418 | 117 | °C |
HDPE M5370P塑料供应商,长期销售美国利安德巴塞尔生产的HDPE原料,以上是“HDPE Alathon® M5370P”塑胶料的物性表参数.近期代理商可转仓交易:韩国GS加德士 PP均聚 Caltex PP M560 流动性高,抗撞击性高,注射成型 电气元件,汽车领域的应用,家电部件,工业应用,电池盒
韩国现代 PP均聚 Hyundai EP PPF HT240 均聚物,耐用性
美国RheTech PP共聚 RheTech Polypropylene HP514-182UV 填料,滑石填料,14%填料按重量.
德国爱彼斯 PP均聚 ALTECH® PP-H A 2030/250 GF30 CP 填料,玻璃纤维增强材料,30%填料按重量.
美国利安德巴塞尔 PP共聚 Hifax CA 1210 G 1740
澳大利亚凯诺斯 PP共聚 PROTEQ™ C24UST5L
日本SPDC LLDPE QAMAR FC21HN 通用,中等透明度,抗结块性,光滑性,吹塑薄膜 通用,薄膜
土耳其石化PETKIM LDPE PETILEN H5-21T 流动性低,注射成型,薄膜挤出,吹塑成型 复合,母料
韩国乐天化学 HDPE TITANEX® HM4560UA
匈牙利MOL HDPE TIPELIN® BS 520-14
韩国Hanwha(韩华) HDPE Hanwha Total PE B220A 超高抗冲击性,良好的感官特征,食品接触的合规性,高拉伸强度,优良外观,高密度,耐洗涤剂,可加工性良好,吹塑成型 吹塑成型应用,瓶子
旭川化学 PUR XCB-30 抗溶剂性
北欧化工 PP EE189HPB 16%矿物填料特性,刚性良好,抗撞击性良好,可回收材料,耐刮擦性 汽车内部零件,汽车领域的应用
利安德巴塞尔 PP TBC 172N 矿物填料,20%填料按重量,尺寸稳定性良好,冲击改性,刚性高,刚性良好,共聚物,激光标记,抗撞击性高,流动性中等,延展性 汽车领域的应用
爱彼思 PA6 A 2015/310 GF15 玻纤增强
● HDPE LG化学 BE0300
成型性、耐冲击性、落下冲击强度及耐环境应力龟裂性都很优秀,主要用于制作要求高强度、高密度吹塑成型的HDPE产品。 产品,商标Lutene
● HDPE 美国陶氏 7808 其它
● HDPE 美国陶氏 DGDA-2490 NT
挤出
● HDPE 埃克森美孚 AA48-002
产品商标Exxonmobil
● HDPE 日本三菱 BS003E
中空