其它 其它 吹塑 | |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
比重 | ASTM D-792 | 0.918 | g/cm3 | |
熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 1 | g/10min |
电影穿刺能源 | 20.3um | Internal Method | 3.39 | J |
电影穿刺能源 | 50.8um | Internal Method | 5.08 | J |
电影穿刺力 | 20.3um | Internal Method | 40 | N |
电影穿刺力 | 50.8um | Internal Method | 71.2 | N |
电影穿刺抵抗 | 20.3um | Internal Method | 20.9 | J/cm3 |
电影穿刺抵抗 | 50.8um | Internal Method | 13 | J/cm3 |
电影韧性(MD) | 20.3um | ASTM D-882 | 295 | J/cm3 |
电影韧性(TD) | 20.3um | ASTM D-882 | 341 | J/cm3 |
电影韧性(MD) | 50.8um | ASTM D-882 | 253 | J/cm3 |
电影韧性(TD) | 50.8um | ASTM D-882 | 289 | J/cm3 |
割线模量-2% Secant(MD) | 20.3um | ASTM D-882 | 204 | MPa |
割线模量-2% Secant(TD) | 20.3um | ASTM D-882 | 233 | MPa |
割线模量-2% Secant(MD) | 50.8um | ASTM D-882 | 199 | MPa |
割线模量-2% Secant(TD) | 50.8um | ASTM D-882 | 183 | MPa |
拉伸屈服强度(MD) | 20.3um | ASTM D-882 | 16 | MPa |
拉伸屈服强度(TD) | 20.3um | ASTM D-882 | 15.4 | MPa |
拉伸屈服强度(MD) | 50.8um | ASTM D-882 | 12.2 | MPa |
拉伸屈服强度(TD) | 50.8um | ASTM D-882 | 11 | MPa |
拉伸断裂强度(MD) | 20.3um | ASTM D-882 | 60.7 | MPa |
拉伸断裂强度(TD) | 20.3um | ASTM D-882 | 48.2 | MPa |
拉伸断裂强度(MD) | 50.8um | ASTM D-882 | 40.8 | MPa |
拉伸断裂强度(TD) | 50.8um | ASTM D-882 | 46.9 | MPa |
拉伸断裂伸长率(MD) | 20.3um | ASTM D-882 | 580 | % |
拉伸断裂伸长率(TD) | 20.3um | ASTM D-882 | 800 | % |
拉伸断裂伸长率(MD) | 50.8um | ASTM D-882 | 700 | % |
拉伸断裂伸长率(TD) | 50.8um | ASTM D-882 | 850 | % |
落锤冲击(MD) | 20.3um | ASTM D-1709A | 94 | g |
落锤冲击(TD) | 20.3um | ASTM D-1709B | <100 | g |
落锤冲击(MD) | 50.8um | ASTM D-1709A | 130 | g |
落锤冲击(TD) | 50.8um | ASTM D-1709B | 270 | g |
埃尔曼多夫撕裂强度(MD) | 20.3um | ASTM D-1922 | 300 | g |
埃尔曼多夫撕裂强度(TD) | 20.3um | ASTM D-1922 | 670 | g |
埃尔曼多夫撕裂强度(MD) | 50.8um | ASTM D-1922 | 820 | g |
埃尔曼多夫撕裂强度(TD) | 50.8um | ASTM D-1922 | 1200 | g |
密封起始温度 | 20.3um | Internal Method | 110 | ℃ |
密封起始温度 | 50.8um | Internal Method | 120 | ℃ |
密封强度 | 150℃,0.0203mm | Internal Method | 1000 | g |
密封强度 | 150℃,0.0508mm | Internal Method | 2100 | g |
维卡软化点 | ASTM D-1525 | 103 | ℃ | |
熔化温度 | Internal Method | 124 | ℃ | |
光泽度 | 20°,20.3um | ASTM D-2457 | 62 | |
光泽度 | 20°,50.8um | ASTM D-2457 | 90 | |
光泽度 | 45°,20.3um | ASTM D-2457 | 50 | |
光泽度 | 45°,50.8um | ASTM D-2457 | 61 | |
雾度 | 20.3um | ASTM D-1003 | 12 | % |
雾度 | 50.8um | ASTM D-1003 | 18 | % |
LLDPE HS-7028 NT 7塑料供应商,长期销售美国陶氏生产的LLDPE原料,以上是“LLDPE HS-7028 NT 7”塑胶料的物性表参数.近期代理商可转仓交易:法国道达尔 PP PPH 7069 注塑 纤维长丝和短纤维地毯
韩国PolyMirae PP HP652P 良好的可纺性 地毯
美国福禄 HIPS RPP30EU59HB BLACK 填料/玻璃纤维加固补强,填充30%重量
汪洋高分子 TPE WY1060BT 透明,笔杆专用料,电动工具配件,医用,运动器材,注塑
卡梅尔烯烃 LDPE 600 好的刚度和中等熔体流动速率 盖,集装箱,玩具,化合物,色母
埃及OPC PP MD35 良好的加工性能
美国RTP PC 300 TFE 10 Z 注塑
路博润 TPU 54610 CB 280 导电性,芳香,良好的表面光洁度
美国TLC POM AC-80/TF/15 注塑
美国RTP PA66 227H 增强,高抗冲,注塑
美国RTP PA66 205 TFE 3 SI 玻纤增强,注塑
美国RTP PA6 PA6 20 GF BLK 其它
美国福禄 PA66 RNY15MS01GY 增强,注塑
普立万 PC/PBT XT XT-500-CX00 注塑
美国TPC PA66 GB30 L 润滑
● LLDPE 美国利安德巴塞尔 Petrothene GA501041
● LLDPE 美国利安德巴塞尔 Petrothene GA594000
快的成型周期,优良外观,抗弯曲,共聚物,流动性高,食品接触的合规性,注射成型
● LLDPE 马来西亚大藤 LF0754
特性:突出的冲击强度和撕裂强度
● LLDPE 利安德巴塞尔 GA601033
良好的耐热密封、良好的强度、良好的韧性
● LLDPE 沙特sabic 318BJ
丁烯共聚单体光学性能抗穿孔性 抗氧化性可加工性,良好良好的撕裂强度 热稳定性,良好