抗撞击性,良好,降噪,良好耐磨损性,低摩擦系数 | |
齿轮,汽车内部零件,薄壁部件,轴承 | |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
比重 | ASTMD792 | 0.966 | g/cm3 | |
收缩率-流动(2.00mm) | ASTMD955 | 1.8 | % | |
MoldingShrinkage-AcrossFlow(2.00mm) | ASTMD955 | 1.6 | % | |
吸水率(24hr) | ASTMD570 | 0.010 | % | |
抗张强度2(断裂,23°C) | ASTMD638 | 47.0 | MPa | |
伸长率2(断裂,23°C) | ASTMD638 | 10 | % | |
FlexuralModulus3(23°C,3.00mm,48.0mmSpan) | ASTMD790 | 1620 | MPa | |
FlexuralStrength3(Yield,23°C,3.00mm,48.0mmSpan) | ASTMD790 | 38.0 | MPa | |
NotchedIzodImpact(23°C,2.00mm) | ASTMD256 | 190 | J/m | |
洛氏硬度(R级) | ASTMD785 | 51 | ||
载荷下热变形温度(0.45MPa,未退火) | ASTMD648 | 80.0 | °C | |
维卡软化温度 | ASTMD15254 | 130 | °C | |
线形热膨胀系数-流动 | ASTMD696 | 1.3E-4 | cm/cm/°C | |
体积电阻率 | ASTMD257 | 1.0E+17 | ohmscm | |
介电强度 | ASTMD149 | 44 | kV/mm | |
介电常数(23°C) | ASTMD150 | 2.40 | ||
耗散因数(1MHz) | ASTMD150 | 1.0E-4 | ||
FlameRating(1.6mm) | UL94 | HB |
HDPE L5000塑料供应商,长期销售日本三井生产的HDPE原料,以上是“HDPE LUBMER™ L5000”塑胶料的物性表参数.近期代理商可转仓交易:泰国石化 PP均聚 POLIMAXX 1100PK
美国塞拉尼斯 PP均聚 Celstran® PP-GF20-02 Natural
韩国现代 PP均聚 Hyundai EP PPF HG940 填料,玻璃纤维增强材料.滤材
美国福禄 PP均聚 GAPEX® RPP40DA11NA 填料,玻璃纤维增强材料,40%填料按重量.
法国TOTAL石化 PP共聚 TOTAL Polypropylene Lumicene® MR 110MC2
美国利安德巴塞尔 PP共聚 Hostacom TRC 399N G14008
俄罗斯Nizhnekamskneftekhim PP共聚 NEFTEKHIM PP 8548V
美国纳新 LLDPE HIVAL® 106033 抗紫外线性能良好,己烯共聚单体,抗氧化性,滚塑成型 通用
伊朗扎木石化 LLDPE Jam PE 25525 丁烯共聚单体,注射成型 盖子
伊朗扎木石化 HDPE Jam HDPE HF7750M 单丝
俄罗斯喀山石化 HDPE Kazan HDPE 293-2B5D
意大利API SEBS DP2718/55P0M 低的压缩变形性,抗紫外线性能良好,可回收材料,可加工性良好,快的成型周期,耐臭氧性能,耐低温,耐化学性良好,耐碱,耐气候影响性能良好,耐热性高,耐酸,耐洗涤剂
德国Akro-Plastic PA610 S3 GF 50 1 natural (3533) 玻纤增强,高刚性,高强度,抗化学性,热稳定 电器,汽车,外壳
普利朗 PA6 RB306G6 其它
● HDPE 韩国韩华 CHNA-8380
具有优秀的物理与电气特性,优秀的抗氧化性与强韧性,优秀的ESCR/TSCR,加工性能与高速挤出加工型,优秀的耐热性,添加剂:氧化防止剂
● HDPE 美国利安德巴塞尔 Petrothene KR92717
高分子量,抗紫外线性能良好,良好的加工稳定性,挤出
● HDPE 德国赫斯特 A6042P
刚性良好
● HDPE 利安德巴塞尔 GF7740F2.QA
窄分子量分布
● HDPE 美国陶氏 UNIVAL DMDB-6200 NT 7