流动性高,抗紫外线性能良好,脱模性能良好 注射成型 | |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
比重 | ASTMD792 | 1.20 | g/cm3 | |
熔流率(熔体流动速率)(300°C/1.2kg) | ASTMD1238 | 25 | g/10min | |
收缩率-流动(3.20mm) | InternalMethod | 0.50to0.70 | % | |
拉伸模量2 | ASTMD638 | 2370 | MPa | |
抗张强度3(屈服) | ASTMD638 | 62.1 | MPa | |
抗张强度3(断裂) | ASTMD638 | 65.5 | MPa | |
伸长率3(屈服) | ASTMD638 | 6.0 | % | |
伸长率4(断裂) | ASTMD638 | 110 | % | |
弯曲模量4(50.0mm跨距) | ASTMD790 | 2310 | MPa | |
弯曲强度4(屈服,50.0mm跨距) | ASTMD790 | 93.1 | MPa | |
悬壁梁缺口冲击强度(23°C) | ASTMD256 | 640 | J/m | |
装有测量仪表的落镖冲击(23°C,EnergyatPeakLoad) | ASTMD3763 | 54.2 | J | |
拉伸冲击强度5 | ASTMD1822 | 378 | kJ/m2 | |
载荷下热变形温度(1.8MPa,未退火,6.40mm) | ASTMD648 | 127 | °C | |
线形热膨胀系数-流动(-40到40°C) | ASTME831 | 7.0E-5 | cm/cm/°C | |
线形热膨胀系数-横向(-40到40°C) | ASTME831 | 6.8E-5 | cm/cm/°C | |
透射率(2540um) | ASTMD1003 | 88.0 | % | |
雾度(2540um) | ASTMD1003 | 1.0 | % |
PC HF1130RC compound塑料供应商,长期销售沙伯基础生产的PC原料,以上是“PC LNP™ COLORCOMP™ HF1130RC compound”塑胶料的物性表参数.近期代理商可转仓交易:意大利Guarniflon PTFE Flontech® FT-BRR40-2 填料,青铜填料,40%填料按重量.
意大利拉题 PPS Latiohm 80-04 PD01 G/30 填料,玻璃纤维增强材料,30%填料按重量.
日本三井 TPX TPX® DX310 刚性良好,注射成型,纤维,纺纱,挤出,挤出涂层
沙伯基础 PC LNP™ STAT-KON™ DEF13 compound
德国爱彼斯 PC ALCOM® LD2 PC 1000 UV 14001 WT1007-14 填料,ALBIS,德国爱彼斯.Lighting,Applications,汽车领域的应用
日本三菱 PC XANTAR® MX 1061 抗紫外线性能良好,很高的粘度,挤出
日本三菱 PC XANTAR® G4F 23 R 填料,玻璃纤维增强材料,20%填料按重量.
印度Ester PBT ESTOPLAST EP 4020 填料,玻璃纤维增强材料.
Chem Polymer公司 PA66 Chemlon® 533 G 填料,玻璃纤维增强材料,33%填料按重量.
美国Infinity LTL PA66 INSTRUC PA66GF10
比利时Ravago PA66 Hylon® N1033THL 填料,玻璃纤维增强材料,33%填料按重量.
斯洛伐克Plastcom PA66 SLOVAMID® 66 GF 25
斯洛伐克Plastcom PA66 SLOVAMID® 66 BT TS
以色列屹立 PA66 FRIANYL® A3 N V0
印度SRF PA6 TUFNYL® SGF25BNATURAL
● PC 沙伯基础 LEXAN 263R resin
中等粘性,可加工性良好,注射成型
● PC 德国拜耳 3107 其它
● PC 沙伯基础 LEXAN OQ2720 resin
● PC 美国陶氏 201-15
特性:提供优质的耐热性能、良好的透明度和极高的耐冲击强度等物理机械性能。
● PC 三菱工程塑料 MB2112N
阻燃,抗化学性