性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
比重 | ASTMD792 | 1.19 | g/cm3 | |
密度 | ISO1183 | 1.20 | g/cm3 | |
熔流率(熔体流动速率)(300°C/1.2kg) | ASTMD1238 | 18 | g/10min | |
溶化体积流率(MVR)(300°C/1.2kg) | ISO1133 | 17.0 | cm3/10min | |
收缩率-流动(3.20mm) | InternalMethod | 0.55to0.75 | % | |
MoldingShrinkage-AcrossFlow(3.20mm) | InternalMethod | 0.60to0.80 | % | |
吸水率(饱和,23°C) | ISO62 | 0.13 | % | |
吸水率(平衡,23°C,50%RH) | ISO62 | 0.11 | % | |
拉伸模量2 | ASTMD638 | 2400 | MPa | |
拉伸模量 | ISO527-2/1 | 2300 | MPa | |
抗张强度3(屈服) | ASTMD638 | 67.0 | MPa | |
拉伸应力(屈服) | ISO527-2/50 | 63.0 | MPa | |
抗张强度3(断裂) | ASTMD638 | 54.0 | MPa | |
拉伸应力(断裂) | ISO527-2/50 | 57.0 | MPa | |
伸长率3(屈服) | ASTMD638 | 6.0 | % | |
拉伸应变(屈服) | ISO527-2/50 | 6.0 | % | |
伸长率4(断裂) | ASTMD638 | 80 | % | |
拉伸应变(断裂) | ISO527-2/50 | 73 | % | |
弯曲模量4(50.0mm跨距) | ASTMD790 | 2400 | MPa | |
弯曲模量5 | ISO178 | 2400 | MPa | |
FlexuralStress5,6 | ISO178 | 96.0 | MPa | |
弯曲强度4(屈服,50.0mm跨距) | ASTMD790 | 103 | MPa | |
简支梁缺口冲击强度7 | -30°C | ISO179/1eA | 10 | kJ/m2 |
简支梁缺口冲击强度7 | 23°C | ISO179/1eA | 59 | kJ/m2 |
简支梁无缺口冲击强度7 | -30°C | ISO179/1eU | NoBreak | |
简支梁无缺口冲击强度7 | 23°C | ISO179/1eU | NoBreak | |
悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 100 | J/m |
悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 600 | J/m |
悬壁梁缺口冲击强度8 | -30°C | ISO180/1A | 9.0 | kJ/m2 |
悬壁梁缺口冲击强度8 | 23°C | ISO180/1A | 55 | kJ/m2 |
悬壁梁缺口冲击强度 | -30°C | ASTMD4812 | NoBreak | |
悬壁梁缺口冲击强度 | 23°C | ASTMD4812 | NoBreak | |
无缺口伊佐德冲击强度8 | -30°C | ISO180/1U | NoBreak | |
无缺口伊佐德冲击强度8 | 23°C | ISO180/1U | NoBreak | |
装有测量仪表的落镖冲击(23°C,TotalEnergy) | ASTMD3763 | 80.0 | J | |
载荷下热变形温度(0.45MPa,未退火,3.20mm) | ASTMD648 | 130 | °C | |
HeatDeflectionTemperature9(0.45MPa,Unannealed,100mmSpan) | ISO75-2/Be | 131 | °C | |
载荷下热变形温度(1.8MPa,未退火,3.20mm) | ASTMD648 | 120 | °C | |
HeatDeflectionTemperature9(1.8MPa,Unannealed,100mmSpan) | ISO75-2/Ae | 121 | °C | |
维卡软化温度 | ASTMD152510 | 136 | °C | |
维卡软化温度 | —— | ISO306/B50 | 139 | °C |
维卡软化温度 | —— | ISO306/B120 | 140 | °C |
BallPressureTest(125°C) | IEC60695-10-2 | Pass | ||
线形热膨胀系数-流动(-40到40°C) | ASTME831 | 6.8E-5 | cm/cm/°C | |
线形热膨胀系数-流动(23到80°C) | ISO11359-2 | 7.7E-5 | cm/cm/°C | |
线形热膨胀系数-横向(-40到40°C) | ASTME831 | 7.0E-5 | cm/cm/°C | |
CLTE-Transverse(23to80°C) | ISO11359-2 | 8.0E-5 | cm/cm/°C | |
RTIElec | UL746 | 130 | °C | |
RTIImp | UL746 | 120 | °C | |
RTIStr | UL746 | 130 | °C | |
介电常数(1.10GHz) | ASTMES7-83 | 2.79 | ||
耗散因数(1.10GHz) | ASTMES7-83 | 5.6E-3 | ||
UL阻燃等级 | 0.40mm | UL94 | V-2 | |
UL阻燃等级 | 1.2mm | UL94 | V-1 | |
UL阻燃等级 | 1.5mm | UL94 | V-0 | |
灼热丝易燃指数(1.6mm) | IEC60695-2-12 | 960 | °C | |
热灯丝点火温度(1.5mm) | IEC60695-2-13 | 850 | °C | |
透射率 | 1000um | InternalMethod | >90.0 | % |
透射率 | 2000um | InternalMethod | >89.0 | % |
PC CFR9111 resin塑料供应商,长期销售沙伯基础生产的PC原料,以上是“PC LEXAN™ CFR9111 resin”塑胶料的物性表参数.近期代理商可转仓交易:韩国乐天化学 PBT Infino GP-5300G 填料,玻璃纤维增强材料.
美国塞拉尼斯 PPS Celstran® PPS-CF40-01 填料,长碳素纤维,40%填料按重量.
丹麦UNIFLON PTFE Uniflon COMP LUB 良好的流动性
沙伯基础 PPA LNP™ LUBRICOMP™ UX05051 compound 填料,玻璃纤维增强材料.
美国塞拉尼斯 LCP Vectra® E531i 填料,矿物填料.
沙伯基础 PPO(PPE) NORYL™ 6390C resin
美国杜邦 POM均聚 Delrin® PC691 NC010 成核的,低粘度,注射成型 医疗/护理用品
韩国工程塑料 POM共聚 Kepital® F40-03
韩国乐天化学 PC Infino EF-1032 无卤,阻燃性,挤出
意大利Soredi PC Niblend F17 填料,玻璃纤维增强材料,17%填料按重量.
沙伯基础 PC LEXAN™ HF1130 resin 尺寸稳定性良好,高耐热性,尺寸稳定性良好,清晰度高,清晰度高,高耐热性,注射成型,注射成型
美国Polymer Resources PBT PRL TP-G20 填料,玻璃纤维增强材料,20%填料按重量.
日本三菱 PC XANTAR® 24 U 中等粘性,抗紫外线性能良好
韩国LG化学 PA66 Lumid® GP2300BW 填料,玻璃纤维增强材料,30%填料按重量.电气元件
德国Bada PA66 Badamid® C70 M40 MoS2 填料,矿物填料,40%填料按重量.