低粘度,延展性,抗撞击性,高 注射成型 | |
汽车领域的应用 | |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
比重 | ASTMD792 | 1.14 | g/cm3 | |
熔流率(熔体流动速率)(260°C/5.0kg) | ASTMD1238 | 9.0 | g/10min | |
收缩率-流动(3.20mm) | InternalMethod | 0.50to0.70 | % | |
吸水率(24hr) | ASTMD570 | 0.10 | % | |
吸水率(平衡,23°C) | ASTMD570 | 0.40 | % | |
拉伸模量2 | ASTMD638 | 2210 | MPa | |
抗张强度3(屈服) | ASTMD638 | 56.5 | MPa | |
伸长率3(屈服) | ASTMD638 | 5.0 | % | |
伸长率4(断裂) | ASTMD638 | 150 | % | |
弯曲模量4(50.0mm跨距) | ASTMD790 | 2340 | MPa | |
弯曲强度4(屈服,50.0mm跨距) | ASTMD790 | 86.2 | MPa | |
悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 530 | J/m |
悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 640 | J/m |
装有测量仪表的落镖冲击 | -30°C,TotalEnergy | ASTMD3763 | 54.2 | J |
装有测量仪表的落镖冲击 | 23°C,TotalEnergy | ASTMD3763 | 61.0 | J |
载荷下热变形温度(0.45MPa,未退火,3.20mm) | ASTMD648 | 124 | °C | |
载荷下热变形温度 | 1.8MPa,未退火,3.20mm | ASTMD648 | 107 | °C |
载荷下热变形温度 | 1.8MPa,未退火,6.40mm | ASTMD648 | 110 | °C |
线形热膨胀系数-流动(-40到40°C) | ASTME831 | 7.2E-5 | cm/cm/°C | |
导热系数 | ASTMC177 | 0.20 | W/m/K |
PC MC8002 resin塑料供应商,长期销售沙伯基础生产的PC原料,以上是“PC CYCOLOY™ MC8002 resin”塑胶料的物性表参数.近期代理商可转仓交易:日本三井 TPE ADMER™ NF912E 良好粘结性,食品接触的合规性,挤出 薄膜,食品服务领域,非特定食品应用
美国Teknor Apex TPE Elexar® EL-8730R
丹麦UNIFLON PTFE Fluoroplex B 60 - GMA 填料,UNIFLON,丹麦UNIFLON.
德国恩欣格 PEI HYDEL® PEI-7
韩国乐天化学 PPA Infino HX-4300G 填料,玻璃纤维增强材料.
美国RTP POM共聚 RTP EMI 861 填料,不锈钢纤维,10%填料按重量.
德国巴斯夫 POM共聚 Ultraform® N 2640 Z4 BK140 Q600
沙伯基础 PC LNP™ STAT-KON™ DE0069F compound
美国普立万 PC Edgetek™ CY1000-20GF/000 BK005 填料,玻璃纤维增强材料,20%填料按重量.
沙伯基础 PC CYCOLOY™ CY5120 resin 无溴,无氯,阻燃性,注射成型
中国苏州奥美 PC omay® V42B 环保,阻燃性
荷兰Witcom PBT Witcom PBT 6G/3L1 填料,玻璃纤维增强材料,30%填料按重量.
法国Eurostar PA66 6/Starflam RFB247EX 填料,玻璃珠玻璃纤维.
美国RTP PBT RTP 1002 填料,玻璃纤维增强材料,15%填料按重量.
Chem Polymer公司 PA66 Chemlon® 100 X 润滑,高强度,通用,可加工性良好,韧性良好,注射成型 电器用具,汽车领域的应用,电气/电子应用领域
● PC 瑞士科莱恩 Clariant PC PC-1100H30
填料:碳纤维增强材料, 30% 填料按重量。
● PC 美国盛禧奥 CALIBRE 351-10
脱模性能良好,防潮,高耐热性,耐蒸汽
● PC 美国RTP RTP 385 HEC
填料:镀镍碳纤维, 30% 填料按重量。
● PC 沙伯基础 LEXAN LUX9612 resin
无溴,无氯,阻燃性,良好的流动性,注射成型
● PC 沙伯基础 XYLEX FXY330DF resin
注射成型