符合 ECO,毒性低,低烟度,阻燃性 注射成型 | |
填料:玻璃纤维增强材料, 10% 填料按重量。 |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
比重 | ASTMD792 | 1.40 | g/cm3 | |
熔流率(熔体流动速率)(337°C/6.6kg) | ASTMD1238 | 13 | g/10min | |
拉伸模量2 | ASTMD638 | 4480 | MPa | |
抗张强度3(屈服) | ASTMD638 | 106 | MPa | |
抗张强度3(断裂) | ASTMD638 | 102 | MPa | |
伸长率4(断裂) | ASTMD638 | 8.0 | % | |
FlexuralModulus4(100mmSpan) | ASTMD790 | 4830 | MPa | |
FlexuralStrength4(Yield,100mmSpan) | ASTMD790 | 189 | MPa | |
悬壁梁缺口冲击强度(23°C) | ASTMD256 | 59 | J/m | |
ReverseNotchIzodImpact(3.20mm) | ASTMD256 | 400 | J/m | |
载荷下热变形温度(1.8MPa,未退火,6.40mm) | ASTMD648 | 208 | °C | |
FAAFlammability5 | FAR25.853 | NATURAL | ||
NBSSmokeDensity | Flaming,Dmax | ASTME662 | 5.00 | |
NBSSmokeDensity | Flaming,Ds,1.5min | ASTME662 | 0.00 | |
NBSSmokeDensity | Flaming,Ds,4min | ASTME662 | 5.00 | |
OSU峰值放热速率6 | FAR25.853 | 36.0 | kW/m2 | |
OSU总放热量7 | FAR25.853 | 6.00 | kWmin/m2 |
PEI AR9110 resin塑料供应商,长期销售沙伯基础生产的PEI原料,以上是“PEI ULTEM™ AR9110 resin”塑胶料的物性表参数.近期代理商可转仓交易:美国Cereplast PLA Cereplast Compostables® 1006
土耳其Elastron TPV Elastron® V V201.A78.B 抗紫外线性能良好,柔软,可粘结性,高耐热性,挤出,注射成型
美国OMNI TPO OmniPro™ TPO 6M SCR 抗撞击性高,良好的流动性,耐刮擦性,注射成型
美国Teknor Apex TPE Monprene® PR-23040
德国凯柏胶宝 TPE THERMOLAST® K TC4TPN (Series: GP/AP)
美国Teknor Apex TPE Sarlink® TPE ME-2259D BLK 288 注射成型 汽车外部零件
土耳其Elastron SEBS Elastron® G G400.A30.T 可粘结性,嵌段共聚物,柔软,注射成型
意大利Versalis EPDM Dutral® TER 4437 WO
美国Techmer PPSU HiFill® PPSU 4000 BK 注射成型
美国RTP PEEK RTP 2285 HF 填料,碳纤维增强材料,30%填料按重量.
美国RTP PPS RTP EMI 1363 填料,不锈钢纤维,20%填料按重量.
韩国三养 PC TRIREX® Compound 3025N2 阻燃性
德国ROMIRA PPO(PPE) Luranyl® HT 190 高耐热性,注射成型
美国NEXT Specialty POM共聚 NEXT REGRIND POMC TX90-100RG 共聚物,冲击改性,良好的成型性能 汽车领域的应用
美国塞拉尼斯 POM共聚 Hostaform® C 9021 GV1/20 XGM
● PEI 美国RTP RTP 2100 AR 15 TFE 15
填料:芳族聚酰胺纤维, 15% 填料按重量。
● PEI 美国RTP 2103 Z
玻纤增强
● PEI 美国RTP 2199 X 89189 C
碳纳米填充,静态导电,抗ESD
● PEI 沙伯基础(原GE) 1000-1000
具体技术指数参照1000
● PEI 美国RTP 2285 A
注塑